Description
A high-temperature composite filament for end-use applications
Raise3D Industrial PPA GF is a glass fiber reinforced composite filament material based on PPA (polyphthalamide or high-performance/high-temperature Nylon). PPA is distinguished from aliphatic polyamides (e.g.PA6) by higher melting point, glass transition temperatures (Tg), lower moisture absorption, and greater dimensional stability. The incorporation of short glass fibers further improves upon the properties of PPA matrix, which makes PPA GF printed parts promising for end-use applications in automotive, aerospace, electrical and electronics (E&E) industry.
- High rigidity and strength
- Excellent thermal performance
- Lower moisture absorption
- Dimensional stability
- Chemical resistance
- Higher heat distortion temperatures
- cost-effective
Compatibility: Raise3D Industrial PPA Support Filament
- Applications
- Automobile
- Aerospace
- Electrical and electronics (E&E) industry
- End-use parts
Printing Guide
Recommended Print Settings
Nozzle temperature (°C) 280-320℃
Bed temperature (°C) 65-80℃
Layer height (mm) 0.1-0.25 mm
Printing speed (mm/s) 30-120 mm/s
Cooling fan OFF
Drying temperature (°C) 80-100°C for 4 to 6 hours
Printing Notifications:
Abrasion of the brass nozzle happens frequently when printing PPA GF. Using abrasion resistance nozzle, such as hardened steel and above grade nozzles, is highly recommended.
After the printing, it is recommended to anneal the model in the oven at 80-100°C for 4 to 8 hours and cool the room temperature naturally.
Raise3D Industrial PPA GF Filament
Color:
Natural (PMS: 11-0602 TPX / RAL: 9016)
Orange (PMS: 151C)
Specifications: 1.75 mm/ 1 kg
Raise3D Industrial PPA GF is a glass fiber-reinforced composite filament material based on PPA (polyphthalamide or high-performance/high-temperature Nylon). PPA can be distinguished from aliphatic polyamides (e.g.PA6) by a higher melting point, glass transition temperatures (Tg), lower moisture absorption, and greater dimensional stability. The incorporation of short glass fibers further improves upon the properties of PPA matrix, which makes PPA GF printed parts promising for end-use applications in the automotive, aerospace, electrical and electronics (E&E) industries.
This filament is compatible with Raise3D Industrial PPA Support Filament.
Due to the higher fiber content of PPA filaments, when printing PPA CF and PPA GF, an extra wear-resistant nozzle and extrusion system are required for a consistent printing performance. The E2CF and the RMF500 are specially designed for printing high-performance fiber-reinforced composite filaments. As such, it is recommended to use the Raise3D Industrial PPA CF filament and PPA GF filament exclusively on the E2CF and the RMF500.